Zihard® High Temperature PMI Foam
Zihacell® High Temperature PMI Foam (suffix HT): Suitable for epoxy, bisphenol A, and cyanoacrylate resin systems that can be co-cured at temperatures up to 180-200°C. It has been applied in high-end equipment manufacturing fields such as high-performance antenna covers.
Mean performance of Zihacell® High Temperature PMI Foam
| Density(kg/m³) | Model |
Compression Strength
(MPa)
|
Compression Modulus
(MPa)
|
Tensile Strength
(MPa)
|
Tensile Modulus
(MPa)
|
Elongation at Break
(%)
|
Shear
Strength
(MPa)
|
Shear
Modulus
(MPa)
|
Bending
Strength
(MPa)
|
Flexural Modulus
(MPa)
|
Compressive
Strength
(MPa)
|
Compressive
Modulus
(MPa)
|
Dimensional
Change Rate
(Absolute %)
|
| Test Standard | GB/T 8813-2008 | GB/T 9641-1988 | GB/T 1455-2005 | GB/T 8812.2-2007 | GB/T 8813-2008 | GB/T 8811-2008 | |||||||
| 75 | XK75-HT | 1.4 | 90 | 1.8 | 95 | 2.4 | 1.3 | 45 | 3.1 | 120 | 0.8 | 50 | 0.6 |
| CK72-HT | 1.25 | 55 | 1.7 | 98 | 2 | 1.2 | 36 | 2.5 | 98 | 0.65 | 30 | 0.6 | |
| 110 | CX110-HT | 3.2 | 105 | 3 | 140 | 2.2 | 2.1 | 68 | 5.4 | 140 | 1.2 | 60 | 0.6 |
| XK110-HT | 3.4 | 140 | 3.5 | 160 | 2.5 | 2.4 | 70 | 5.5 | 185 | 1.45 | 80 | 0.6 | |
| CK110-HT | 3.2 | 100 | 3 | 170 | 2.21 | 2.2 | 65 | 5.4 | 166 | 1.2 | 65 | 0.6 | |